佐伯 誠一; 瀬古 典明; 笈田 多加史*; 山岸 宏造*
no journal, ,
For more practical use of polyethylene terephthalate (PET) waste materials, they should be modified and functionalized in spite of its poor reactivity derived from chemical stability. In this study, we adopted radiation-induced grafting method as a powerful modification tool for functionalization of PET fiber, and tried to synthesize amine type metal adsorbents for newly effective reuse of waste PET materials. At radiation-grafting experiments, glycidyl methacrylate was grafted on PET fiber irradiated with electron beam, and the degree of grafting reached to around 10%. The grafted samples were aminated in 50% ethylene diamine in 2-propanol solution at 40 or 60C for 15 or 60 minutes. At 60C and 60 minutes for amination process, the resultant samples lost 9% weight by alkali hydrolysis. For evaluating metal adsorption capacity, the aminated fiber put into 100 ppb vanadium aqueous solution and shaked over night, and then the vanadium concentration of the residual solution were evaluated by ICP-MS. The adsorption capacity of the aminated PET fiber showed around 0.9 g-V/kg-adsorbent except for 0.06 g-V/kg-adsorbent of the sample aminated at 40C and 15 minutes. As a result, amine type metal adsorbents based on PET materials were synthesized by radiation-induced grafting method taking into account for proper amination process.
植木 悠二; 保科 宏行; 佐伯 誠一; 瀬古 典明
no journal, ,
シリコンウエハーのエッチング溶液として使用される高濃度アルカリ溶液には、ppbレベルの銅イオンが不純物として含まれている。この銅イオンは、ウエハー表面上に小さな凹凸を作る原因となるため、生産効率の低下を招く。そのため、pH15以上の強アルカリ条件下でも機能する新規金属吸着材の開発が切望されている。そこで我々は、放射線エマルショングラフト重合と2,2'-イミノジエタノール(IDE)によるアミノ化処理により、pH3から15の範囲で機能する繊維状金属吸着材の開発を行った。その結果、pH15における銅吸着容量は0.41mmol/g-吸着材であり、2個のIDE基により1個の銅イオンを捕らえることが分かった。この吸着材の強アルカリ条件下における吸着容量は、中性域(pH5.7)の値に対し1/3に減少したが、実用的には十分な金属吸着容量を示すことがわかった。